Degradation of LDPE LLDPE and HDPE in film extrusion

Andersson, Thorbjorn and Wesslén, Bengt LU (2003) Proceedings of the 2003 TAPPI European PLACE Conference In TAPPI European PLACE Conference 2. p.333-359
Abstract
The degradation of different polyethylenes, LDPE, LLDPE, and HDPE, with and without antioxidants and at different oxygen concentrations in the polymer granulates have been studied in extrusion coating processing. The degradation was followed by On Line Rheometry, Size Exclusion Chromatography, Surface Oxidation Index measurements, and GC-MS Chromatography. The degradations starts in the extruder where primary radicals are formed which are subject the auto oxidation when oxygen is present. In the extruder, cross-linking and chain scission reactions are dominating at low and high melt temperatures, respectively, for LDPE, and chain scission is over all dominating for the more linear LLDPE and HDPE resins. Additives such as antioxidants react... (More)
The degradation of different polyethylenes, LDPE, LLDPE, and HDPE, with and without antioxidants and at different oxygen concentrations in the polymer granulates have been studied in extrusion coating processing. The degradation was followed by On Line Rheometry, Size Exclusion Chromatography, Surface Oxidation Index measurements, and GC-MS Chromatography. The degradations starts in the extruder where primary radicals are formed which are subject the auto oxidation when oxygen is present. In the extruder, cross-linking and chain scission reactions are dominating at low and high melt temperatures, respectively, for LDPE, and chain scission is over all dominating for the more linear LLDPE and HDPE resins. Additives such as antioxidants react with primary radicals formed in the melt. Degradation taking place in the film between the die orifice and the quenching point is mainly related to the exposure time to air-oxygen. Melt temperatures above 280 (Less)
Please use this url to cite or link to this publication:
author
organization
publishing date
type
Chapter in Book/Report/Conference proceeding
publication status
published
subject
keywords
Polymer melts, Surface oxidation, Film blowing
in
TAPPI European PLACE Conference
volume
2
pages
333 - 359
publisher
TAPPI
conference name
Proceedings of the 2003 TAPPI European PLACE Conference
external identifiers
  • scopus:1342324957
language
English
LU publication?
yes
id
ff5e3955-6c3b-49e6-bd20-6b8bad9d77ff (old id 612908)
date added to LUP
2007-11-28 09:28:43
date last changed
2017-02-19 04:28:53
@inproceedings{ff5e3955-6c3b-49e6-bd20-6b8bad9d77ff,
  abstract     = {The degradation of different polyethylenes, LDPE, LLDPE, and HDPE, with and without antioxidants and at different oxygen concentrations in the polymer granulates have been studied in extrusion coating processing. The degradation was followed by On Line Rheometry, Size Exclusion Chromatography, Surface Oxidation Index measurements, and GC-MS Chromatography. The degradations starts in the extruder where primary radicals are formed which are subject the auto oxidation when oxygen is present. In the extruder, cross-linking and chain scission reactions are dominating at low and high melt temperatures, respectively, for LDPE, and chain scission is over all dominating for the more linear LLDPE and HDPE resins. Additives such as antioxidants react with primary radicals formed in the melt. Degradation taking place in the film between the die orifice and the quenching point is mainly related to the exposure time to air-oxygen. Melt temperatures above 280},
  author       = {Andersson, Thorbjorn and Wesslén, Bengt},
  booktitle    = {TAPPI European PLACE Conference},
  keyword      = {Polymer melts,Surface oxidation,Film blowing},
  language     = {eng},
  pages        = {333--359},
  publisher    = {TAPPI},
  title        = {Degradation of LDPE LLDPE and HDPE in film extrusion},
  volume       = {2},
  year         = {2003},
}