Destabilization of fcc stable materials during SPD under high pressure
(2004) Ultrafine Grained Materials III, 2004 p.401-404- Abstract
It was shown that of a fine α-phase was formed in the Hadfield steel after a cold plastic deformation to E = 50%. Nuclei of the ex-phase of deformed samples reduced the decomposition start temperature of the austenite by 180°C. Fine crystals of an α-phase nearly 30 nm in size, whose concentration was as high as ∼2.3%, were detected in a steel Fe 79.55Mn17Al3Co0.45 after a SPD to ε = 92%. A steel Fe61.2Cr18Mn20N 0.7C0.1 contained fine crystals of a strain-induced α-phase 20 nm in size after a low temperature plastic deformation. The α-phase, which was formed under the given conditions, had an extremely low Curie temperature TC =... (More)
It was shown that of a fine α-phase was formed in the Hadfield steel after a cold plastic deformation to E = 50%. Nuclei of the ex-phase of deformed samples reduced the decomposition start temperature of the austenite by 180°C. Fine crystals of an α-phase nearly 30 nm in size, whose concentration was as high as ∼2.3%, were detected in a steel Fe 79.55Mn17Al3Co0.45 after a SPD to ε = 92%. A steel Fe61.2Cr18Mn20N 0.7C0.1 contained fine crystals of a strain-induced α-phase 20 nm in size after a low temperature plastic deformation. The α-phase, which was formed under the given conditions, had an extremely low Curie temperature TC = 400°C. When the steel was strongly deformed (e ≈ 8) by SPD a strain-induced α-phase have a normal Curie temperature TC = 600°C. Thus, the obtained results indicate that SPD can result in a considerable destabilization of stable austenitic steels.
(Less)
- author
- Efros, Boris ; Beygelzimer, Yakiv ; Deryagin, Anatoly ; Efros, Nataly ; Pilyugin, Vitaly and Orlov, Dmitry LU
- publishing date
- 2004
- type
- Chapter in Book/Report/Conference proceeding
- publication status
- published
- subject
- keywords
- Magnetic properties, Severe plastic deformation, Stable austenitic steels, Structure
- host publication
- Ultrafine Grained Materials III
- editor
- Zhu, Y.T. ; Langdon, T.G. ; Valiev, R.Z. ; Lee Semiatin, S. and et al, al
- pages
- 4 pages
- conference name
- Ultrafine Grained Materials III, 2004
- conference location
- Charlotte, NC., United States
- conference dates
- 2004-03-14 - 2004-03-18
- external identifiers
-
- scopus:3042819564
- ISBN
- 0873395719
- language
- English
- LU publication?
- no
- id
- 78b55fef-50a4-45f5-821c-db395b4aeb61
- date added to LUP
- 2016-06-20 15:45:34
- date last changed
- 2022-03-08 19:19:33
@inproceedings{78b55fef-50a4-45f5-821c-db395b4aeb61, abstract = {{<p>It was shown that of a fine α-phase was formed in the Hadfield steel after a cold plastic deformation to E = 50%. Nuclei of the ex-phase of deformed samples reduced the decomposition start temperature of the austenite by 180°C. Fine crystals of an α-phase nearly 30 nm in size, whose concentration was as high as ∼2.3%, were detected in a steel Fe <sub>79.55</sub>Mn<sub>17</sub>Al<sub>3</sub>Co<sub>0.45</sub> after a SPD to ε = 92%. A steel Fe<sub>61.2</sub>Cr<sub>18</sub>Mn<sub>20</sub>N <sub>0.7</sub>C<sub>0.1</sub> contained fine crystals of a strain-induced α-phase 20 nm in size after a low temperature plastic deformation. The α-phase, which was formed under the given conditions, had an extremely low Curie temperature T<sub>C</sub> = 400°C. When the steel was strongly deformed (e ≈ 8) by SPD a strain-induced α-phase have a normal Curie temperature T<sub>C</sub> = 600°C. Thus, the obtained results indicate that SPD can result in a considerable destabilization of stable austenitic steels.</p>}}, author = {{Efros, Boris and Beygelzimer, Yakiv and Deryagin, Anatoly and Efros, Nataly and Pilyugin, Vitaly and Orlov, Dmitry}}, booktitle = {{Ultrafine Grained Materials III}}, editor = {{Zhu, Y.T. and Langdon, T.G. and Valiev, R.Z. and Lee Semiatin, S. and et al, al}}, isbn = {{0873395719}}, keywords = {{Magnetic properties; Severe plastic deformation; Stable austenitic steels; Structure}}, language = {{eng}}, pages = {{401--404}}, title = {{Destabilization of fcc stable materials during SPD under high pressure}}, year = {{2004}}, }