Quantum Dots Sensitized ZnO Nanowires Solar Cells

Abdelwahab, Abdalla LU (2012) KEMN10 20121
Department of Chemistry
Abstract
In this project, solar cell based on CdSe quantum dots sensitized onto ZnO nanowires was well fabricated. The following quantum dot-nanowire linker molecules were used: 3- mercaptoproponic acid (3-MPA) and 2-mercaptoproponic acid (2-MPA). The best solar cell efficiency was observed with 3-MPA linker molecule. Solar cell efficiency for different lengths of ZnO NWs and different sensitization times was also investigated.
Please use this url to cite or link to this publication:
author
Abdelwahab, Abdalla LU
supervisor
organization
course
KEMN10 20121
year
type
H2 - Master's Degree (Two Years)
subject
keywords
Nanokemi
language
English
id
2857137
date added to LUP
2012-06-29 17:14:05
date last changed
2012-06-29 17:14:05
@misc{2857137,
  abstract     = {{In this project, solar cell based on CdSe quantum dots sensitized onto ZnO nanowires was well fabricated. The following quantum dot-nanowire linker molecules were used: 3- mercaptoproponic acid (3-MPA) and 2-mercaptoproponic acid (2-MPA). The best solar cell efficiency was observed with 3-MPA linker molecule. Solar cell efficiency for different lengths of ZnO NWs and different sensitization times was also investigated.}},
  author       = {{Abdelwahab, Abdalla}},
  language     = {{eng}},
  note         = {{Student Paper}},
  title        = {{Quantum Dots Sensitized ZnO Nanowires Solar Cells}},
  year         = {{2012}},
}